K-200 Feldspar
Mol. Weight: 591.6
Category Feldspar
Fill Oxides KNO
Molecular Analysis:
K20 0.690 Al2O3 1.049 SiO2 6.648
Na2O 0.286 Fe2O3 0.002 LOI 0.059
CaO 0.024
|
Top
Percentage Analysis
67.49 % SiO2
18.07 % Al2O3
10.98 % K2O
3.00 % Na2O
0.23 % CaO
0.05 % Fe2O3
0.18 % L.O.I.
|
|
Kaolin
Mol. Weight: 270.41
Category Clay
Fill Oxides Al2O3
Molecular Analysis:
K20 0.011 Al2O3 1.000 SiO2 2.098
CaO 0.012 Fe2O3 0.009 TiO2 0.012
MgO 0.011 P2O5 0.004
|
Top
Percentage Analysis
46.62 % SiO2
37.71 % Al2O3
0.40 % K2O
0.16 % MgO
0.25 % CaO
0.18 % P2O5
0.51 % Fe2O3
0.36 % TiO2
13.80 % L.O.I.
|
|
Kaopaque 20
Mol. Weight: 258.20
Category Clay
Fill Oxides Al2O3
Molecular Analysis:
K20 0.001 Al2O3 1.000 SiO2 1.944
Na2O 0.001 Fe2O3 0.005 TiO2 0.022
CaO 0.010
MgO 0.002
|
Top
Percentage Analysis
45.24 % SiO2
39.49 % Al2O3
0.03 % K2O
0.03 % Na2O
0.03 % MgO
0.21 % CaO
0.32 % Fe2O3
0.67 % TiO2
13.99 % L.O.I.
|
|
Kaopaque
Mol. Weight: 258.82
Category Clay
Fill Oxides Al2O3
Molecular Analysis:
K20 0.004 Al2O3 1.000 SiO2 1.947
Na2O 0.001 Fe2O3 0.004 TiO2 0.031
CaO 0.010
MgO 0.000
|
Top
Percentage Analysis
45.19 % SiO2
39.39 % Al2O3
0.13 % K2O
0.03 % Na2O
0.01 % MgO
0.21 % CaO
0.25 % Fe2O3
0.96 % TiO2
13.84 % L.O.I.
|
|
Kentucky
Old Mine #4 Ball Clay
Mol. Weight: 374.79
Category Clay
Fill Oxides Al2O3
Molecular Analysis:
K20 0.044 Al2O3 1.000 SiO2 3.488
Na2O 0.012 Fe2O3 0.026 TiO2 0.056
CaO 0.027
MgO 0.037
|
Top
Percentage Analysis
55.90 % SiO2
27.20 % Al2O3
1.10 % K2O
0.20 % Na2O
0.40 % MgO
0.40 % CaO
1.10 % Fe2O3
1.20 % TiO2
12.50 % L.O.I.
|
|
Kentucky
Stone Clay
Mol. Weight: 490.12
Category Clay
Fill Oxides Al2O3
Molecular Analysis:
K20 0.068 Al2O3 1.000 SiO2 5.485
Na2O 0.008 Fe2O3 0.040 TiO2 0.086
CaO 0.026
MgO 0.061
|
Top
Percentage Analysis
67.21 % SiO2
20.80 % Al2O3
1.30 % K2O
0.10 % Na2O
0.50 % MgO
0.30 % CaO
1.29 % Fe2O3
1.40 % TiO2
7.10 % L.O.I.
|
|
Kingman
Potash Feldspar
Mol. Weight: 587.5
Category Feldspar
Fill Oxides KNO
Molecular Analysis:
K20 0.742 Al2O3 1.026 SiO2 6.583
Na2O 0.237 Fe2O3 0.004
CaO 0.021
|
Top
Percentage Analysis
67.30 % SiO2
17.80 % Al2O3
11.90 % K2O
2.50 % Na2O
0.20 % CaO
0.10 % Fe2O3
0.20 % L.O.I.
|
|
Kona
A-3 Feldspar
Mol. Weight: 668.37
Category Feldspar
Fill Oxides KNO
Molecular Analysis:
K20 0.549 Al2O3 1.062 SiO2 7.961
Na2O 0.391 Fe2O3 0.004
CaO 0.060
|
Top
Percentage Analysis
71.54 % SiO2
16.20 % Al2O3
7.74 % K2O
3.62 % Na2O
0.50 % CaO
0.10 % Fe2O3
0.30 % L.O.I.
|
|
Kona
F-4 Soda Feldspar
Mol. Weight: 547.1
Category Feldspar
Fill Oxides KNO
Molecular Analysis:
K20 0.279 Al2O3 1.042 SiO2 6.152
Na2O 0.565 Fe2O3 0.002
CaO 0.156
|
Top
Percentage Analysis
67.54 % SiO2
19.41 % Al2O3
4.81 % K2O
6.40 % Na2O
1.60 % CaO
0.05 % Fe2O3
0.20 % L.O.I.
|
|
Kyanite
Mol. Weight: 172.78
Category Clay
Fill Oxides Al2O3
Molecular Analysis:
K20 0.006 Al2O3 1.000 SiO2 1.102
Na2O 0.006 Fe2O3 0.011 TiO2 0.026
|
Top
Percentage Analysis
38.30 % SiO2
59.00 % Al2O3
0.30 % K2O
0.20 % Na2O
1.01 % Fe2O3
1.20 % TiO2
|
|
Kyanite-Calcined
Mol. Weight: 170.03
Category Clay
Fill Oxides Al2O3
Molecular Analysis:
K20 0.004 Al2O3 1.000 SiO2 1.087
Na2O 0.006 Fe2O3 0.006 TiO2 0.014
CaO 0.001
MgO 0.000
|
Top
Percentage Analysis
38.40 % SiO2
59.95 % Al2O3
0.20 % K2O
0.21 % Na2O
0.01 % MgO
0.03 % CaO
0.54 % Fe2O3
0.67 % TiO2
|